Chinese   English
   
Home About Us Products Honor Equipment News Apply Messages Recruitment Contact Us
Products
HEX BOLT
HEX NUT
SOCKET CAP SCREW
STRUCTURE BLOT
OTHER
 
Equipment
Hex nut machine -41B
Hex nut machine -41B

Thread rolling machine
Thread rolling machine

Rolling Machine
Rolling Machine

Rolling Machine
Rolling Machine

Thread rolling machine
Thread rolling machine

Multi-station cold heading machine precision
Multi-station cold heading machine precision

Multi-station cold heading machine precision
Multi-station cold heading machine precision

Special equipment for forging
Special equipment for forging

Special equipment for forging
Special equipment for forging

 
Contact Us
Address : Southwest Develop Area Of Yongnian Handan Hebei China
Tel : 86-0310-6639608
Fax : 86-0310-6639608
E-mail : admin@hsfastener.net
Contact : MR Dong
 
News
What materials are used for high strength bolts
 

. The maximum tensile strength of materials used for high-strength bolts has a great relationship with quenching treatment. Generally, it is difficult to meet the material requirements of class 10.9s high-strength bolts after 40Cr quenching treatment.In addition to the different properties in the treatment process, the delayed fracture properties of high-strength bolts with different materials under high stress are also different.

2. The 40Cr high-strength bolt is mainly used in the bolt ball node network frame, and its design strength is generally 390MPa(d>=30mm) or 430MPa (d <30mm), without high pre-tensile stress in use.Attention should be paid to understanding and ensuring the delayed fracture performance when applying high pretension.The delayed fracture performance of 20MnTiB high strength bolt is better than that of 40B.

3. According to GB/ t1231-91, the recommended materials of 10.9S bolt are 20MnTiB (applicable specification <=M24) and 35VB(applicable specification <=M30).In quenching, large-diameter high-strength bolts are not easy to be fully quenched, so generally do not use large-diameter high-strength bolts, if you want to use, you should reduce its working stress.

Mechanical properties of bolts, screws and studs of carbon steel and alloy steel - marking:

(1) carbon steel and alloy steel bolts, screws and studs (screw diameter of 1.6-39mm, operating temperature of -50 ° c -- 300 ° c) have a total of 10 performance grade marking codes, namely 3.6, 4.6, 4.8, 5.6, 5.8, 6.8, 8.8, 9.8, 10.9 and 12.9 (bolts, screws and studs made of free-cutting steel shall not exceed 250 ° c).Among them, the bolts of grade 8.8 and above are made of low carbon alloy steel or medium carbon steel and are heat-treated (quenching and tempering), generally called high-strength bolts, and the rest are commonly called ordinary bolts.

(2) bolt performance grade label is composed of two parts, which respectively represent the nominal tensile strength value and bending strength ratio of bolt materials.

For example, a bolt with performance grade 4.6 means:

A. the nominal tensile strength of bolt material reaches 400MPa;

B. The bending strength ratio of bolt material is 0.6;

C. Nominal yield strength of bolt material reaches 400×0.6=240MPa class

Performance grade 10.9 high strength bolt, its material after heat treatment, can achieve:

A. The nominal tensile strength of bolt material reaches 1000MPa;

B. The bending strength ratio of bolt material is 0.9;

C. Nominal yield strength of bolt material reaches 1000×0.9=900MPa class.

 